ExxonMobil™ LDPE LD 151 Series
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TYelQH_ExxonMobil-LDPE-LD-151-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LD 151 series low density polyethylene grade well combines high transparency and high stiffness. According to the requirements of surface performance, some additive components can be added. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 370 | MPa | ASTM D882 |
| 1% secant, TD | 370 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| TD : Yield | 15.0 | MPa | ASTM D882 |
| MD : Fracture | 22.0 | MPa | ASTM D882 |
| TD : Fracture | 18.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 430 | % | ASTM D882 |
| TD : Fracture | 560 | % | ASTM D882 |
| Dart Drop Impact | 55 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 95 | g | ASTM D1922 |
| TD | 170 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 73 | ASTM D2457 | |
| Haze | 6.0 | % | ASTM D1003 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekudur MW/GF 30 | TEKUMA Kunststoff GmbH | PBT | Tekudur |
| Novalloy-S S66S4 | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| Cri-Line IF-715 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Neoflex™ 8085 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |
| Dryflex® VE 65A101 | ELASTO | TPV | Dryflex® |