Alathon® M6080UV
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TXrqhA_Alathon-M6080UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M6080UV is a narrow molecular weight distribution homopolymer that exhibits enhanced flow characteristics and good balance of stiffness and impact resistance. Typical applications include cases, tote bins, crates and trays. M6080UV contains a UV stabilizer for outdoor applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.9 | g/10 min | ASTM D1238 |
| Spiral Flow | 21.8 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1020 | MPa | |
| 1% Secant | 845 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 29.3 | MPa | |
| Break | 15.9 | MPa | |
| Tensile Elongation 3(Break) | 380 | % | ASTM D638 |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1410 | MPa | |
| 1% Secant | 1310 | MPa | |
| 2% Secant | 1020 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 23 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Peak Melting Temperature | 133 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 116 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E80E | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| APEX® 130-P | Teknor Apex Company | PVC, Flexible | APEX® |
| EVALENE® HDPE HJ04601 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |
| Ferro PP TPP34AN54NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| EPIMIX PBT GV0 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |