ACCUCOMP™ POL052L
| Category: | PC , Polycarbonate |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TVf8ke_ACCUCOMP-POL052L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUCOMP™ POL052L is a Polycarbonate (PC) product. It is available in North America. Primary characteristic: high viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 66.0 | MPa | |
| Break | 65.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 75 | % | |
| Break | 130 | % | |
| Flexural Modulus | 2700 | MPa | ASTM D790 |
| Flexural Strength | 97.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 950 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 125 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ranger PBT PBT-403-M-G30 HF | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Medalist® MD-325 | Teknor Apex Company | TPE | Medalist® |
| Borealis PE CT7200 | Borealis AG | PE Homopolymer | Borealis PE |
| Generic Silicone - Aluminum | Generic | Silicone | Generic |