SABIC® LLDPE 726 Series
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TV7Kis_SABIC-LLDPE-726-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description 726 series resins are fractional index Linear Low Density Polyethylene grades suitable for blown film applications. Films produced using these resins gives relatively higher stiffness, good tensile properties, impact strength and sealing properties. 726 Series includes following grades:
Typical Applications Bread bags, textile and garment packaging, shipping sacks, can liners carrier bags etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm | 300 | MPa | |
| 1% Secant, TD : 30 µm | 320 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 30 µm | 13.0 | MPa | |
| TD : Yield, 30 µm | 12.0 | MPa | |
| MD : Break, 30 µm | 42.0 | MPa | |
| TD : Break, 30 µm | 36.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 600 | % | |
| TD : Break, 30 µm | 750 | % | |
| Dart Drop Impact (30 µm) | 85 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm | 85 | g | |
| TD : 30 µm | 250 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm) | 75 | ASTM D2457 | |
| Haze (30.0 µm) | 13 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (30.0 µm) | 620 | J/cm | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 195 to 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Celcon® LW90-F2 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| DENKA ABS K-5130G | Denka Company Limited | ABS | DENKA ABS |
| Generic PEKK | Generic | PEKK | Generic |
| KEBATER® PBT BFA20 | BARLOG plastics GmbH | PBT | KEBATER® |
| Magnobond 106-167 | Magnolia Plastics, Inc. | Epoxy | Magnobond |