Next PC CX-02GY
| Category: | PC , Polycarbonate |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TUUZlX_Next-PC-CX-02GY.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PC UnFilled Grey Compound (RAL-7035) Product Applications Electrical/Electronics, Housing Appliance & Industrial Application Benefits High Flow, Good dimensional stability, High heat resistance |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation 1 | 0.35 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | ASTM D256 | ||
| -30°C | 11.0 | kJ/m² | |
| 23°C | 72.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 140 | °C | |
| 1.8 MPa, Unannealed | 124 | °C | |
| Vicat Softening Temperature | 142 | °C | ASTM D1525 |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 270 to 280 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apirex® MBL 35 UV | API SpA | TPU-Polyether | apirex® |
| DENYL 6 5040 | Vamp Tech | Nylon 6 | DENYL |
| Hifax TYL 250P | LyondellBasell Industries | PP, Unspecified | Hifax |
| Karina STRAW PVC COMPOUND 751-38/117-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH T16020 | Polykemi AB | PP Homopolymer | POLYfill |