PELPRENE™ P280B
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TU3bd8_PELPRENE-P280B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™P280B is a thermoplastic polyester elastomer (TPEE) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.6 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 37.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 494 | MPa | ASTM D790 |
| Compressive Modulus | 35.0 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 8.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% Strain) | 28.4 | MPa | ASTM D412 |
| Tear Strength | 206 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 199 | °C | ASTM D1525 |
| Melting Temperature | 218 | °C | DSC |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Hardness, JIS k6301, A scale: 9910% Compression Modulus, ASTM D695: 35 MPaResilience, JIS K6301: 55 %Coefficient of Linear Thermal Expansion, TMA: 14e-5 1/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polyethylene E206-01 | RheTech, Inc. | LLDPE | RheTech Polyethylene |
| Sindustris PC GN1003FS | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| WELLAMID Nylon 6600 GS 15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Baydur® 645 (25 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Daelim Po1y® PP-180 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |