Mediprene® OF 600M
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ELASTO |
| Trademark: | Mediprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TT02MH_Mediprene-OF-600M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Mediprene oil free compounds were developed to address demands for transparent medical thermoplastic elastomer (TPE) grades with a minimum of potential extractables and leachables. The Mediprene OF range, helps to prevent the possibility of oil migrating or leaching out of the material, a key requirement for medical and healthcare-related devices. They are ideal for sensitive medical applications where transparency is also required. Regulatory compliance Representative Mediprene grades have passed cytotoxicity tests according to ISO 10993-5 and are compliant with USP Class VI. Mediprene TPE materials are PVC, silicone and latex free, making them allergen free and a viable alternative to PVC based compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 4.00 mm) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 9.00 | MPa | |
| 100% Strain | 1.60 | MPa | |
| 300% Strain | 2.80 | MPa | |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 30.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature 1 | -50 to 125 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 180 to 230 | °C | |
| Front Temperature | 180 to 230 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 210 | °C | |
| Cylinder Zone 2 Temp. | 150 to 210 | °C | |
| Cylinder Zone 3 Temp. | 150 to 210 | °C | |
| Cylinder Zone 4 Temp. | 150 to 210 | °C | |
| Cylinder Zone 5 Temp. | 150 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Unstressed Material |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDB 502 Phillips Process | Marco Polo International, Inc. | HDPE | MARPOL® |
| MBA PS 3124 (China) | MBA Polymers | PS (GPPS) | MBA PS |
| Next PMMA AX-01RD.(MH-4152) | Next Polymers Ltd. | Acrylic (PMMA) | Next PMMA |
| KOPLA PA66 KDP1200 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LNP™ LUBRICOMP™ DCP32 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |