Edgetek™ SF-40GF/000 RS NC
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TRZgAI_Edgetek-SF-40GF-000-RS-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass Fiber Reinforced PPS Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 - 0.55 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 190 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3 | 15000 | MPa | ASTM D790 |
| Flexural Strength 4 | 275 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 700 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 274 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 300 - 320 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| LUVOCOM® 6-8159 | Lehmann & Voss & Co. | Nylon 12 | LUVOCOM® |
| Osterlene® LD-1-919 | Osterman & Company | LDPE | Osterlene® |
| Petrotene® PP A3 G20 BRC0001 PH321 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Petrothene® LB560200 | LyondellBasell Industries | HDPE | Petrothene® |
| RTP 205 A TFE 5 HI | RTP Company | Nylon 6 | RTP |