Petrotene® PP A2 T20 PRTA011 PH202
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TR8INW_Petrotene-PP-A2-T20-PRTA011-PH202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 20% mineral reinforced for injection molding, resistant to oil, grease and many solvents, good set of mechanical properties and dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 to 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.2 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.020 | % | ASTM D570 |
| Ash Content | 18 to 22 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 50°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 2 | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 68.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 90.0 | °C | ASTM D1525 3 |
| -- | 140 | °C | ASTM D1525 4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2°C/min |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zenite® 6330 | Celanese Corporation | LCP | Zenite® |
| UNITIKA Nylon 6 A3130HR-25 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| Nymax™ GF1200 A13 HS NC067 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Jiangsu Meilan XXMLF3-10 | Jiangsu Meilan Chemical Co., Ltd. | Fluorelastomer | Jiangsu Meilan |
| Karina YELLOW PVC COMPOUND 902-02/232-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |