Order Products : sales@su-jiao.com
Lupox® TE5000SZ
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TPhdbz_Lupox-TE5000SZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupox®TE5000SZ is a polycarbonate polybutene terephthalate (PC PBT) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupox®The main features of the TE5000SZ are:
Lupox®The typical application fields of TE5000SZ are: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 150 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 540 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 115 | °C | ASTM D648 |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 255 - 265 | °C | |
| Nozzle Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.5 mm/min |
| 4 . | 2.5 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6002 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| Sindustris PBT TE5001GH | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| AMTOPP TT25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Globalene® TPV 1087A BK | Lee Chang Yung Chemical Industry Corp. | TPV | Globalene® |
| Lupol® GP2300 | LG Chem Ltd. | PP, Unspecified | Lupol® |