LNP™ THERMOCOMP™ RF0029S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TP551S_LNPTHERMOCOMPRF0029Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1002 FR HS Product reorder name: RF0029S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.90 - 1.1 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 - 1.4 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.98 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 6370 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 101 | MPa | ASTM D638 |
| Yield | 102 | MPa | ISO 527-2 |
| Fracture | 101 | MPa | ASTM D638 |
| Fracture | 102 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 2.5 | % | ASTM D638, ISO 527-2 |
| Fracture | 2.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 5900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 152 | MPa | ASTM D790 |
| -- | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 500 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.50 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 249 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 234 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 219 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 2200 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| Stat-Tech™ ST3200-0005 ES RS | PolyOne Corporation | PC | Stat-Tech™ |
| Staramide PK005EI2 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Kepital® FL2020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Karina ORANGE COLOR CONCENTRATE -E 32/ 34-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |