Toyolac® ASG-30
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TOgcI6_Toyolac-ASG-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® ASG-30 is a Styrene Acrylonitrile (SAN) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| 23°C | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.30 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 125 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 135 | MPa | ASTM D638 |
| 23°C | 124 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break, 23°C | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9400 | MPa | ASTM D790 |
| 23°C | 10500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 160 | MPa | ASTM D790 |
| 23°C | 188 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, 12.7 mm) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 111 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 to 105 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® MX 2032 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Borealis PP BC545MO | Borealis AG | PP Impact Copolymer | Borealis PP |
| DENISTAT M 00U 09 E | Vamp Tech | Acetal (POM) Copolymer | DENISTAT |
| LEXAN™ 940 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ LUBRICOMP™ WFL36E compound | SABIC Innovative Plastics Europe | PBT | LNP™ LUBRICOMP™ |