EBAC® SP1806
| Category: | EnBA , Ethylene n-Butyl Acrylate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | EBAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TNi2U5_EBAC-SP1806.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Westlake EBAC® SP1806 is an ethylene butyl acrylate copolymer designed for extrusion coating and laminating. SP1806 can also be compounded as an impact modifier or used in highly filled applications. Westlake EBAC® resins are less crystalline and softer than polyethylene and offer compatibility and adhesion to typically difficult to bond to polymers. SP1806 is non-corrosive at extrusion temperatures and has excellent thermal stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.3 | g/10 min | ASTM D1238 |
| n-Butyl Acrylate Content | 17.5 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 40 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 10.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 730 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -73.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 55.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 91.0 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LA70 GF15 HH | Bada AG | Nylon 66 | Badamid® |
| CERTENE™ HGB-0354 | Muehlstein | HDPE | CERTENE™ |
| Karina RED PVC COMPOUND 830-42/16-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina LILAC MBATCH (SP31449)-E 34/182-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RFP36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |