4TECH® 9B20000 E-S
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TNYNvN_4TECH-9B20000-E-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9B20000 E-S is a Standard Flow Unfilled Electro Static PA6 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 2.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 70.0 | MPa | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Melting Temperature 2 | 223 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1387 TFE 15 SI 2 | RTP Company | PPS | RTP |
| SABIC® LDPE 1922N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TEKAPPO™ J910 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Spartech Polycom SCR5-2015 | Spartech Polycom | PP Copolymer | Spartech |
| Unichem 7811G-05 | Colorite Polymers | PVC, Unspecified | Unichem |