Plenco 04301 (Compression)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TMCm8e_Plenco-04301-Compression-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 04301 is a heat resistant, mineral filled phenolic molding compound offering excellent dimensional stability and electrical properties. UL recognized under component file E40654. 04301 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Apparent Density | 0.66 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.44 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10100 | MPa | ASTM D638 |
| Tensile Strength | 56.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 8810 | MPa | ASTM D790 |
| Flexural Strength | 77.6 | MPa | ASTM D790 |
| Compressive Strength | 203 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20.6 | J/m | ASTM D256 |
| Notched Izod Impact | 15 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 198 | °C | ASTM D648 |
| Continuous Use Temperature | 208 | °C | ASTM D794 |
| Thermal Conductivity (100°C) | 0.48 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.9E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.050 | ASTM D150 | |
| Arc Resistance | 148 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index | 32 | % | ASTM D2863 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.17%Heat Resistance, ASTM D794: 208°CDrop Ball Impact, PLENCO Method: 93 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 0.50 | hr | |
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Mold Close Time: 3-8 sec |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinkral® B 732/E | Versalis S.p.A. | ABS | Sinkral® |
| XYRON™ L542Z | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Karina BLACK PVC COMPOUND CAK 851-48/1-F-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 830 12 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |
| MAJORIS DG157 - 8229 | AD majoris | PP, Unspecified | MAJORIS |