CERTENE™ LLBF-220C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TKzKYo_CERTENE-LLBF-220C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-220C is a certified prime resin containing Butene-comonomer, specially designed for production of Blown films for general purpose packaging. LLBF-220C features easy processability with very good film strength as well as wide heat sealing temperature range. LLBF-220C major applications include garment bags, produce bags and liners. Maximum recommended film drawdown is 0.5 mil. LLBF-220C contains medium slip and medium antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 215 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 250 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 25 µm | 45.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 650 | % | ASTM D882 |
| TD : Break, 25 µm | 990 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 80 | g | ASTM D1922 |
| TD : 25 µm | 550 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm) | 65 | ASTM D2457 | |
| Haze (25.4 µm) | 7.0 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1890 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Ultradur® S 4090 G6 High Speed | BASF Corporation | PBT+ASA | Ultradur® |
| Ferro PP NPP00GC25WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| LUVOCOM® 1106-8087/BL/EM | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| TechnoFiber PP LGF 30-10-01 H | TechnoCompound GmbH | PP, Unspecified | TechnoFiber |