SABIC® LDPE HP0823J
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TKdGef_SABIC-LDPE-HP0823J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABlC® LDPE HPO823J is a Low Density Polyethylene grade formulated with slip and anti-block additives. It typically exhibits good melt strength with good draw down ability. Films typically exhibit good toughness and good biaxial shrink properties with low friction and low blocking. TYPICAL APPLICATIONS: Shrink film, thin industrial film, thin packaging film, bags & pouches. This grade enables high speed converting without sticking. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 260 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 11.0 | MPa | ISO 527-2 |
| Coefficient of Friction | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.50 - 4.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 25 - 80 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 24.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 150 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 111 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 40 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 90 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 9.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Measured on 50 micron thickness blown film extruded at melt temperature of 180°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1407 | RTP Company | PESU | RTP |
| RTP 800.5 UV | RTP Company | Acetal (POM) Copolymer | RTP |
| KOPELEN JM-370UN | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Huafon JF-W-3040 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Hybrid S464G20 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |