Orgalloy® LT 4060
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Arkema |
| Trademark: | Orgalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TIugUH_Orgalloy-LT-4060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Orgalloy® LT 4060 is a Polyamide 6 Alloy (Nylon 6 Alloy) product. It can be processed by extrusion, injection molding, profile extrusion, or resin transfer molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1040 | 1040 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/5.0 kg) | 1.70 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | |||
| Saturation | 5.0 | -- | % | |
| Equilibrium | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | -- | 300 | MPa | ISO 527-2 4 |
| Tensile Stress (50% Strain) | -- | 22.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Break) | -- | > 50 | % | ISO 527-2 6 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | |||
| -30°C | -- | 22.0 | kJ/m² | |
| 23°C | -- | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa) | 60.0 | -- | °C | ISO 75-2 8 |
| Melting Temperature 9 | 217 | -- | °C | ISO 11357-3 10 |
| Electrical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Comparative tracking index | -- | 600 | IEC 60112 11 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 12 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 13 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 10 °C/min |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® SM488 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| Axiall PVC 10703 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| KOPA® KN163HI | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Leona™ 14G25 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| OTECH ALLOY OTO8580 - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |