LONGLITE® PBT 2100-104B
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGytb4_LONGLITE-PBT-2100-104B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 2100-104B is an unreinforced flame retarded impact modified black color injection molding grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 to 1.7 | % | |
| Flow | 1.7 to 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 15 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Amilan® CM1011G-15 | Toray Resin Company | Nylon 6 | Amilan® |
| DINAPLEN® PPH1S15 G30 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| LNP™ THERMOCOMP™ LC006EXQ compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Petlon R-Prime B3-G30-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |
| Sylvin 9915-85 Blue 8364 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |