Lifoflex® UVX 27.01 B038-5
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ELASTO |
| Trademark: | Lifoflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGWXha_Lifoflex-UVX-27-01-B038-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
There are many advantages in using polyamide (PA) in an application, including high temperature resistance, a very high strength, a matt surface and excellent stiffness and impact resistance. When combined with Lifoflex PA bonding grades, you get the properties of both materials in one product. These special TPE grades offer excellent bonding to PA6, PA66, PA12 in two component applications. Giving you the advantage of soft-touch qualities without the need for separate primer or adhesive. A high bonding strength is also possible to glass fibre reinforced polyamide materials (up to 40% glass fibre). The outstanding properties of these TPE compounds, such as high service temperature range, high oil resistance, soft touch surface and high flexibility, open up the design possibilities in a wide variety of applications. The Lifoflex PA bonding grades are very easy to process via injection moulding. The wide processing window results in a lower rate of defective parts and faster cycle times. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 27 | DIN 53505 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Flow (Yield) | 3.30 | MPa | DIN 53504 |
| Tensile Elongation - Flow (Break) | 730 | % | DIN 53504 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 11 | % | |
| 70°C, 22 hr | 27 | % | |
| 110°C, 24 hr | 65 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Oil Absorption 1(70°C) | 14 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 72 hr, Motor Oil 5W-30 fully synthetic |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V900 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 2200 TFE 15 | RTP Company | PEEK | RTP |
| Hyundai EP PA66 LD130 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Lucent PP CPP-230 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Sylvin 9077-94 Grey 9527 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |