Star L PPS D93F
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Star L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGNiM4_StarLPPSD93F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Star L PPS D93F is a PTFE / Aramide Lubricated, PPS Injection Molding Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| shrinkage- Flow (4.00 mm) | 0.90 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Flexural Modulus | 4400 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 1.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed, 64.0 mm Span) | 120 | °C | ISO 75-2/Af |
| Melting Temperature (DSC) | 283 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 310 - 320 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Mold Temperature | 135 - 165 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 310 to 320°C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 1001 F | ROMIRA GmbH | ABS | Rotec® ABS |
| Axiall PVC HHP-190 FR Natural | Axiall Corporation | PVC Alloy | Axiall PVC |
| Fluon® PTFE PA1015Z | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| EcoLon® MRGF3013-BK1 | Wellman Engineering Resins | Nylon 66/6 | EcoLon® |
| Ultramid® A3WG10 CR BK00564 | BASF Corporation | Nylon 66 | Ultramid® |