HANWHA 8600L
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TGGqGO_HANWHA-8600L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CLNA-8600L is a low density polyethylene(LDPE) compound designed for the insulation of coaxial cable and radio frequency communication cables. It has excellent electrical properties. CLNA-8600L is commonly used by blending with CHNA-8600H prior to extrusion. Recommended blend ratios of 8600H/8600L/Nucleating agent are 68~78 / 30~20 / 2 %. Applications: 8600H&L can be used coaxial cable and radio frequency(RF) communication cables using a gas injection foaming process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 11.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.28 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 8.0E-5 | ASTM D150 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 200 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF33-66/6 XE-BK167A | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| XYCOMP® 5101 | Greene, Tweed & Co. | PEEK | XYCOMP® |
| ALTECH® PA66 A 2020/109 GF20 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| HIPLEX® HXM 50100 | HIP-PetroHemija | HDPE | HIPLEX® |
| Osterlene® PPH-20-.5 | Osterman & Company | PP Homopolymer | Osterlene® |