Sipolprene® 35180 B
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TG7HC6_Sipolprene-35180-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sipolprene® 35180 B (black color version in dry blend) is an ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 35, a low modulus, and a rheological behaviour, which makes it suitable for injection moulding and extrusion processing. Black colour and/or UV stabilised and/or heat stabilised are all available in dry blend version on request. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption 1(23°C, 24 hr) | 0.73 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 35 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 800 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 45.0 | MPa | ASTM D790, ISO 178 |
| Abrasion Resistance | 26.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 113 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 111 | °C | ISO 306/A50, ASTM D1525 2 |
| Peak Melting Temperature | 177 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Immersion |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® A-361C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| TYNAB® RH36 | Tyne Plastics LLC. | ABS | TYNAB® |
| VALOX™ 176 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| NuSil CV3-1161 | NuSil Technology | Silicone | NuSil |
| Lucent PC PC/PBT-1422 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |