Auracell® MH
| Category: | CA , Cellulose Acetate |
| Manufacturer: | Rotuba Extruders, Inc. |
| Trademark: | Auracell® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TG0hKf_Auracell-MH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Auracell® MH is a Cellulose Acetate (CA) product. It can be processed by injection molding and is available in Europe or North America. Primary characteristic: eco-friendly/green. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 2.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 66 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.2 | MPa | |
| Break, 23°C | 36.2 | MPa | |
| Break, 70°C | 16.2 | MPa | |
| Tensile Elongation (Break) | 43 | % | ASTM D638 |
| Flexural Modulus | 1100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 38.6 | MPa | ASTM D790 |
| Deformation Under Load | ASTM D621 | ||
| 50°C, 6.9 MPa | 1.00 | % | |
| 50°C, 14 MPa | 13.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 59 | J/m | |
| 23°C | 220 | J/m |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Aging - wt. lost, 72 hr (82°C) | 2.6 | wt% | ASTM D706 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flow Beginning Temperature | 150 | °C | ASTM D569 |
| Soluble Matter Loss | 0.40 | % | ASTM D570 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -40.0 to -28.9 | °C | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 193 to 204 | °C | |
| Nozzle Temperature | 199 to 210 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Injection Pressure | 7.58 to 9.65 | MPa | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Vent Depth | 0.051 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ System S110FV | PolyOne Corporation | XLPE | Syncure™ |
| WELLAMID Nylon 6600 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Xuchuan XCW-6020EB | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Elastron® G G400.D40.B | Elastron USA, Inc. | SEBS | Elastron® G |
| POLYFLAM® RIPP 4000 E CS1 | A. Schulman Europe | PP Copolymer | POLYFLAM® |