PRE-ELEC® PBT 1455
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TEoKIN_PRE-ELEC-PBT-1455.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PBT 1455 is a conductive thermoplastic compound based on PBT. Conductivity is achieved by using special conductive carbon black. PRE-ELEC PBT 1455 has excellent mechanical properties as well as good chemical and wear resistance. Typical applications include injection moulded technical parts for areas with explosive atmosphere. PRE- ELEC® PBT 1455 is ideal for the applications where the good mechanical properties of PBT are required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.33 | g/cm³ | ASTM D792 |
| -- | 1.32 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 240°C/10.0 kg | 14 | g/10 min | |
| 240°C/21.6 kg | 60 | g/10 min | |
| Molding Shrinkage - Flow | 1.6 to 2.2 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 39.3 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2 |
| -- | 37.2 | MPa | ASTM D638 |
| 4.00 mm | 37.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break, 4.00 mm | 14 | % | |
| Flexural Modulus (4.00 mm) | 2000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 11 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| 23°C | 11 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 150 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 52.2 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 52.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 219 | °C | ASTM D1525, ISO 306/A50 3 5 |
| -- | 188 | °C | ASTM D1525, ISO 306/B50 4 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 131 to 138 | MPa | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PP TL902 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Network Polymers SMMA MS 125 | Network Polymers, Inc. | Acrylic (SMMA) | Network Polymers SMMA |
| CERTENE™ HI-2553 | Muehlstein | HDPE | CERTENE™ |
| PLUSTEK PA801 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| TECHNYL® A 218 V43 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |