Rynite® FR530 NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TD58AV_Rynite-FR530-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.75 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.15 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 95 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 11200 | MPa | |
| 1000 hr | 9700 | MPa | |
| Flexural Modulus | 10500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 243 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Melting Temperature 1 | 252 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.9E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 2.2E-5 | cm/cm/°C | |
| Transverse | 9.2E-5 | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.8E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.400 mm | 155 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.80 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 100 Hz | 4.80 | IEC 60250 | |
| 1 MHz | 4.70 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.1E-6 | ASTM D150 | |
| 1 MHz | 1.8E-6 | ASTM D150 | |
| 100 Hz | 7.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.350 mm | V-0 | ||
| 1.50 mm | V-0 5VA | ||
| Oxygen Index | 33 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPSiV™ 4000-80A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Elastollan® 695 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| LUVOCOM® TPI-0953 | Lehmann & Voss & Co. | PI, TP | LUVOCOM® |
| LUVOCOM® PEEK CLASSIX 7918 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Sylvin 4200-88 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |