Generic ABS+PC - Unspecified
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TCC1ki_Generic-ABS-PC---Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PC - Unspecified This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 to 1.30 | g/cm³ | ASTM D792 |
| 23°C | 1.18 to 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.35 to 0.50 | % | ASTM D955 |
| 23°C | 0.20 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 to 9000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 55.8 to 65.0 | MPa | ASTM D638 |
| Break, 23°C | 39.0 to 65.4 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.0 to 4.0 | % | |
| Break, 23°C | 2.0 to 37 | % | |
| Flexural Modulus | |||
| 23°C | 3030 to 6890 | MPa | ASTM D790 |
| 23°C | 3330 to 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 84.0 to 116 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.7 to 20 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 47 to 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 to 133 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 83.0 to 130 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 80.0 to 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 to 142 | °C | ISO 306 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 to 5.5E-5 | cm/cm/°C | |
| Transverse | 3.5E-5 to 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 9.8E+15 to 1.0E+16 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 743 to 751 | °C | IEC 60695-2-13 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AW38BK6150 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Aaroprene® CFIPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| POLYCOMPO PE 1300J | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| ALTECH® PP-H A 2020/750 GF20 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Sylvin 3250-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |