PALFORM® R C 09 Datasheet,Acetal (POM) Copolymer,pal plast GmbH-SHANGHAI SUSHENG

Message
PALFORM®R C 09 is a polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in Europe. Typical application areas are: engineering/industrial accessories. Features include: flame retardant/rated flame chemical resistance High stiffness Copolymer Impact resistance

General Information
Features	Rigidity, high Copolymer Solvent resistance Impact resistance, high Good chemical resistance alkali resistance Fuel resistance Hydrolysis resistance
Uses	Gear
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg)	9.50	cm³/10min	ISO 1133
Water Absorption			ISO 62
Saturated, 23°C	0.80	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2700	MPa	ISO 527-2/1A/1
Tensile Stress (Yield, 23°C)	62.5	MPa	ISO 527-2/1A/50
Tensile Strain (Yield, 23°C)	7.5	%	ISO 527-2/1A/50
Nominal Tensile Strain at Break (23°C)	28	%	ISO 527-2/1A/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	170	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	150	°C	ISO 306/B50
Melting Temperature (DSC)	166	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Melt-Volume Flow Rate, ISO 1133, 190°C/2.16 kg: 8 to 11 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2600 to 2800 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 60 to 65 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 6 to 9 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 26 to 30 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 150 to 180 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 6 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 148 to 181 °CDensity, ISO 1183: 1.4 to 1.42 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.7 to 0.9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Melt-Volume Flow Rate, ISO 1133, 190°C/2.16 kg: 8 to 11 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2600 to 2800 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 60 to 65 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 6 to 9 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 26 to 30 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 150 to 180 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 4 to 6 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 148 to 181 °CDensity, ISO 1183: 1.4 to 1.42 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.7 to 0.9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
MARPOL® LDF 723-C	Marco Polo International, Inc.	LDPE	MARPOL®
Tenogel® ABS A3 HS NTLA013 AB329	Petropol Industry and Trade of Polymers LTDA	ABS	Tenogel® ABS
TAROLOY 50 Z1	Taro Plast S.p.A.	PC+PBT	TAROLOY
OTECH ALLOY OL8540 - Profile	OTECH Corporation	TP, Unspecified	OTECH ALLOY
Sylvin 8393-93C Natural	Sylvin Technologies Incorporated	PVC, Semi-Rigid	Sylvin

Category:	Acetal (POM) Copolymer , Acetal (POM) Copolymer
Manufacturer:	pal plast GmbH
Trademark:	PALFORM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	T9pg52_PALFORM-R-C-09.pdf
PRICE:	Order Products email sales@su-jiao.com