Estane® ZHF90AT2 NAT 055
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T9QeW8_EstaneZHF90AT2NAT055.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® ZHF90AT2 NAT 055 is a non halogen, flame retardant, aromatic polyether-based thermoplastic polyurethane. Application: Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 1 sec) | 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | 49.0 | mm³ | ISO 4649-A |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 527-3/200 | ||
| Fracture | 24.0 | MPa | ISO 527-3/200 |
| 50% strain | 9.00 | MPa | ISO 527-3/200 |
| 100% strain | 10.0 | MPa | ISO 527-3/200 |
| 300% strain | 15.0 | MPa | ISO 527-3/200 |
| Tensile Elongation 2(Break) | 460 | % | ISO 527-3/200 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 72 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | V-2 | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 205 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Adapter Temperature | 205 | °C | |
| Die Temperature | 205 | °C |
| Extrusion instructions |
|---|
| Dew Point: -30°C to -40°CDie Tip: 200°C |
| Note Message | |
|---|---|
| 1 . | Type 5A |
| 2 . | Type 5A |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® L-670M | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| LNP™ STAT-KON™ KX02764 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Pinnacle PP 5135C3 | Pinnacle Polymers | PP Random Copolymer | Pinnacle PP |
| EnviroPro 3010GM | West Michigan Compounding | PP Homopolymer | EnviroPro |
| LEXAN™ EXL4016H resin | SABIC Innovative Plastics | PC | LEXAN™ |