| Vyncolit® X655 is a glass fiber and mineral filled phenolic molding compound with excellent dimensional stability and high electrical insulation properties. UL94-listed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ISO 1183 |
| Apparent Density | 1.04 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.15 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.030 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.75 | % | ISO 178 |
| Tensile Modulus (Injection Molded) | 30000 | MPa | ISO 527-2 |
| Tensile Stress (Break, Injection Molded) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 0.45 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 25000 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 185 | MPa | ISO 178 |
| Compressive Stress | 360 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Injection Molded) | 2.7 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (Injection Molded) | 8.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed 1 | > 250 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 211 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed 2 | > 250 | °C | ISO 75-2/C |
| 8.0 MPa, not annealed | 160 | °C | ISO 75-2/C |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 1.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.79 | W/m/K | ASTM E1461 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.1E+13 | ohms | IEC 60093 |
| Volume Resistivity | 5.1E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa | |
| Screw Speed | 50 | rpm |
| Injection instructions |
|---|
| Injection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time: 5 to 12 sec/mm |
| Note Message | |
|---|---|
| 1 . | Postcured up to 210 °C |
| 2 . | Postcured up to 210 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5940 B131 | Spartech Polycom | PP, Unspecified | Spartech |
| Network Polymers LDPE 10 0127 EVA | Network Polymers, Inc. | EVA | Network Polymers LDPE |
| Borealis PP HF700SA | Borealis AG | PP Homopolymer | Borealis PP |
| Aspira™ EB062 | Eastman Chemical Company | Copolyester | Aspira™ |
| Evolue™ SP4530 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |