Staramide AST43
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T6GOrE_Staramide-AST43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide AST43 is a Low Temperature Impact Modified Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.0 to 1.2 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.6 | % | |
| Break | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 2 | ISO 179/1eU | ||
| -30°C | > 100 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -40°C | 30 | kJ/m² | |
| -20°C | 40 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 210 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 80.0 | °C | ISO 75-2/Ae |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 5 | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | ||
| 60 Hz | 2.90 | ||
| 1 MHz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 6.7E-3 | ||
| 60 Hz | 6.7E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 600 | V | |
| Solution B | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 250 to 260 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 275 | °C | |
| Processing (Melt) Temp | 265 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 |
| 5 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AD36BK6052 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Trilene FreeFlow™ 66 | Lion Copolymer, LLC | EPM | Trilene FreeFlow™ |
| Epocast 35-A/9216 | Huntsman Advanced Materials | Epoxy | Epocast |
| KRYSTALFLEX™ PE409 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |
| Sylvin 8225-80 Brown 7429 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |