Moplen RP225M
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T4grsr_Moplen-RP225M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Moplen" RP225M is a controlled rheology medium modified propylene random copolymer for manufacturing high transparent cast films. The product contains slip and anti-block agents. It offers good processability, excellent clarity and gloss and exhibits very good heat weldability. Main applications are packaging of foodstuffs, packaging of stationary, shirts and hosiery. It is also suitable for production of stationary folders. "Moplen" RP225M is suitable for food contact. For regulatory information please refer to "Moplen" RP225M Product Stewardship Bulletin ( PSB ). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/50 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Cast Film | 0.20 | ||
| vs. Itself - Static, Cast Film | 0.20 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus - MD 1(50 µm, Cast Film) | 560 | MPa | ASTM D882 |
| Tensile Strength - MD 2 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 19.4 | MPa | |
| Break, 50 µm, Cast Film | 38.0 | MPa | |
| Tensile Elongation - MD 3 | ASTM D882 | ||
| Yield, 50 µm, Cast Film | 7.6 | % | |
| Break, 50 µm, Cast Film | 740 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 1.5 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 60.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 89 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | < 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 30 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC HDPE PB150 | LG Chem Ltd. | HDPE | SEETEC HDPE |
| DIAMALOY ENGINEERED ALLOYS PCPBT 530 | Network Polymers, Inc. | PC+PBT | DIAMALOY ENGINEERED ALLOYS |
| Kumho STE 1092LP | Korea Kumho Petrochemical Co., Ltd. | Rubber | Kumho STE |
| ISOTHANE® 1055DE | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| Capilene® QC 56 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |