Amodel® A-6135 HN Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Black: A-6135 HN BK 324 Natural A-6135 HS NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Additive	heat stabilizer
Features	Low hygroscopicity Rigidity, high Rigid, good High strength Good creep resistance Good liquidity Good chemical resistance Heat resistance, high Hot water formability Thermal Stability
Uses	Lawn and Garden Equipment Electrical/Electronic Applications Electrical housing Power/other tools Valve/valve components Industrial components Industrial application Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field General Shell
RoHS Compliance	Contact manufacturer
Appearance	Black
Forms	Particle
Processing Method	Water temperature mold injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.45	--	g/cm³	ISO 1183/A
Molding Shrinkage
Flow	0.60	--	%	ASTM D955
Transverse flow	0.90	--	%	ASTM D955
Vertical flow direction	1.0	--	%	ISO 294-4
Flow direction	0.50	--	%	ISO 294-4
Water Absorption
24 hr	0.30	--	%	ASTM D570
23°C, 24 hr	0.29	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	125	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	13800	12200	MPa	ASTM D638
23°C	11500	--	MPa	ISO 527-2
100°C	7310	--	MPa	ISO 527-2
150°C	6270	--	MPa	ISO 527-2
175°C	5310	--	MPa	ISO 527-2
Tensile Stress
Fracture, 23°C	211	--	MPa	ISO 527-2
Fracture, 100°C	121	--	MPa	ISO 527-2
Fracture, 150°C	92.4	--	MPa	ISO 527-2
Fracture, 175°C	82.0	--	MPa	ISO 527-2
--	203	176	MPa	ASTM D638
Tensile Elongation
Fracture	1.9	2.1	%	ASTM D638
Fracture, 23°C	2.0	--	%	ISO 527-2
Fracture, 100°C	4.3	--	%	ISO 527-2
Fracture, 150°C	4.9	--	%	ISO 527-2
Fracture, 175°C	4.7	--	%	ISO 527-2
Flexural Modulus
--	11400	11000	MPa	ASTM D790
23°C	11400	--	MPa	ISO 178
100°C	6600	--	MPa	ISO 178
150°C	4900	--	MPa	ISO 178
175°C	4600	--	MPa	ISO 178
Flexural Strength
--	310	249	MPa	ASTM D790
3.5% strain, 23°C	300	--	MPa	ISO 178
3.5% strain, 100°C	170	--	MPa	ISO 178
3.5% strain, 150°C	123	--	MPa	ISO 178
3.5% strain, 175°C	112	--	MPa	ISO 178
Compressive Strength	148	--	MPa	ASTM D695
Shear Strength	87.6	73.8	MPa	ASTM D732
Poisson's Ratio	0.39	--		ASTM E132

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.2	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	60	--	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	85	69	J/m	ASTM D256
23°C	9.1	--	kJ/m²	ISO 180
Unnotched Izod Impact
--	800	--	J/m	ASTM D256
23°C	62	--	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	303	--	°C	ISO 75-2/B
1.8 MPa, not annealed	288	--	°C	ISO 75-2/A
1.8 MPa, annealed, 3.20mm	291	--	°C	ASTM D648
Melting Temperature	310	--	°C	ASTM D570, ISO 11357-3
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	2.2E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	1.6E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	6.1E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	1.0E-4	--	cm/cm/°C	ASTM E831

Injection	Dry	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Rear Temperature	316 - 321	°C
Front Temperature	327 - 332	°C
Processing (Melt) Temp	321 - 335	°C
Mold Temperature	65.6 - 93.3	°C

Injection instructions
Injection Rate: 3 to 6 in/secHolding Pressure: 50% of injection pressureStorage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Injection Rate: 3 to 6 in/secHolding Pressure: 50% of injection pressureStorage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	T3PUvB_Amodel-A-6135-HN.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP ESD 805	RTP Company	Acetal (POM) Copolymer	RTP
Retpol® PDR 7826 UV2	PolyPacific Pty. Ltd.	Rubber	Retpol®
YUNTIANHUA® M350	YunNan YunTianHua Co., Ltd.	Acetal (POM) Copolymer	YUNTIANHUA®
EMERGE™ PC 8701	Trinseo	PC	EMERGE™
Kazan MDPE PE80B-276	Kazanorgsintez Joint Stock Company	MDPE	Kazan MDPE