YUZEX® 3300
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUZEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T2SGNg_YUZEX-3300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| YUZEX 3300 is a high-density polyethylene resin with narrow molecular weight distribution. So it shows high tenacity, stiffness and very good drawability. Yuzex 3300 gives minimum die drool and excellent thermal stability because of its well designed antioxident package. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | > 30.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 220 | % | ASTM D638 |
| Flexural Modulus | 883 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYPROPYLENE 1102-01 | A. Schulman Inc. | PP, Unspecified | ASI POLYPROPYLENE |
| Geon™ Vinyl Wire & Cable WEMB410B | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Karina IVORY PVC COMPOUND 951-35/4-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP CPP-230 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| OTECH ALLOY OT09060LSZH - Riser Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |