Lumid® HI1102A(W)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T16OF4_Lumid-HI1102A-W-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Impact Applications H/Lamp Screw Mounting |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.6 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.4 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 45 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 80.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 150 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 2.80 | ASTM D150 | |
| Arc Resistance 5 | 195 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure 6 | 0.490 to 1.96 | MPa | |
| Screw Speed | 60 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 23°C |
| 6 . | Hydraulic Type |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 8400K | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Nanjing Hongrui PA66 A353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Boda BDT-KR3752 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| HiFill FR® PA6 FR-N | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Plasmer 1080B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |