Ultramid® 8202C HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0rraz_Ultramid-8202C-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also available in pigmented versions. Applications Ultramid 8202C HS is generally recommended for applications such as gears, valves, fittings, insulators, bushings, slides, window hardware, wiring devices, textile components and furniture casters. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.6 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.6 | -- | % | ISO 62 |
| Saturation | 9.3 | -- | % | ASTM D570 |
| Saturation, 23°C | 9.3 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.6 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -40°C | 4090 | -- | MPa | |
| 23°C | 3700 | 1360 | MPa | |
| 80°C | 750 | -- | MPa | |
| 121°C | 550 | -- | MPa | |
| Tensile Strength | ||||
| Yield, -40°C | 137 | 142 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 90.0 | 48.0 | MPa | ASTM D638 |
| Yield, 80°C | 40.0 | 30.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 121°C | 30.0 | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Yield, 23°C | 88.0 | 43.0 | MPa | ISO 527-2 |
| Break, -40°C | 130 | 80.0 | MPa | ASTM D638 |
| Break, 23°C | 90.0 | 70.0 | MPa | ASTM D638 |
| Break, 80°C | 35.0 | 30.0 | MPa | ASTM D638 |
| Break, 121°C | 25.0 | 20.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, -40°C | 3.0 | 3.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | 22 | % | ASTM D638, ISO 527-2 |
| Yield, 80°C | 25 | 25 | % | ASTM D638 |
| Yield, 121°C | 27 | 30 | % | ASTM D638 |
| Break, -40°C | 5.0 | 3.0 | % | ASTM D638 |
| Break, 23°C | 12 | > 100 | % | ASTM D638 |
| Break, 80°C | > 100 | > 100 | % | ASTM D638 |
| Break, 121°C | > 100 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | 7.0 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -40°C | 3370 | 4200 | MPa | ASTM D790 |
| 23°C | 3170 | 970 | MPa | ASTM D790 |
| 65°C | 600 | -- | MPa | ASTM D790 |
| 90°C | 440 | -- | MPa | ASTM D790 |
| 121°C | 385 | -- | MPa | ASTM D790 |
| 23°C | 2800 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| -40°C | 183 | 168 | MPa | ASTM D790 |
| 23°C | 110 | 42.0 | MPa | ASTM D790 |
| 65°C | 30.0 | -- | MPa | ASTM D790 |
| 121°C | 21.0 | -- | MPa | ASTM D790 |
| 23°C | 95.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 32 | 21 | J/m | |
| 23°C | 48 | 170 | J/m | |
| Drop Impact Resistance (23°C) | 122 | > 271 | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 8.1E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| 6.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.710 mm | 95.0 | -- | °C | |
| 1.50 mm | 105 | -- | °C | |
| 3.00 mm | 105 | -- | °C | |
| 6.00 mm | 105 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength 1(1.50 mm) | 30 | -- | kV/mm | ASTM D149 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.710 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| 6.00 mm | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPU-C75 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Badaflex® TPE-S 40A 1000 | Bada AG | TPE | Badaflex® |
| Aropol™ RTM 80501 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| GLAMIDE® T-714E | TOYOBO America, Inc. | Nylon, Unspecified | GLAMIDE® |
| Rotuba CAB B901 (13% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |