SABIC® PP CX03-82
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0ggNq_SABIC-PP-CX03-82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP CX03-82 is an emission optimised high crystalline copolymer. It offers high impact resistance, in perfect balance with high thermal dimensional stability, stiffness and flow. This for automotive interior applications UV-stabilised material has excellent aesthetic properties as well. It is the obvious alternative to conventional talc-filled copolymers, offering considerable weight saving advantage. SABIC® PP CX03-82 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.6 | % | ASTM D955 |
| 24 hr | 1.6 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 1300 | MPa | ASTM D638 |
| Injection Molded | 1250 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, Injection Molded 2 | 22.0 | MPa | ASTM D638 |
| Yield, Injection Molded | 22.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, Injection Molded 3 | 6.0 | % | ASTM D638 |
| Yield, Injection Molded | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break | ||
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C, Injection Molded | 90 | J/m | ASTM D256A |
| 0°C, Injection Molded | No Break | ASTM D256A | |
| 23°C, Injection Molded | No Break | ASTM D256A, ISO 180/1A | |
| -20°C, Injection Molded | 8.0 | kJ/m² | ISO 180/1A |
| 0°C, Injection Molded | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 145 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 66.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 50.0 | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® E FLF 3624 | A. Schulman Europe | PET | SCHULADUR® |
| Teldene® H03BPM | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| Bayblend® R-FR610 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Karina WHITE COLOR CONCENTRATE 10/1-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SUMIMAC® ECR-9185K | SBHPP | Epoxy | SUMIMAC® |