PRE-ELEC® PP 1384
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0NYNH_PRE-ELEC-PP-1384.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PP 1384 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PP 1384 has excellent mechanical properties and is easy to extrude. PRE-ELEC® PP 1384 is recommended to be used in polypropylene tape co-extrusion for FIBC (type C) applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 1.0 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.2 - 1.7 | % | ASTM D955 |
| Flow direction | 1.2 - 1.7 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 98 | ISO 868 | |
| Shaw D | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Flow | 30.0 | MPa | ASTM D638 |
| -- 1 | 30.0 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 2480 | MPa | ASTM D790 |
| 4.00 mm | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | |||
| -20°C | 2.1 | kJ/m² | ASTM D256 |
| -20°C | 2.0 | kJ/m² | ISO 179 |
| 23°C | 4.0 | kJ/m² | ISO 179 |
| 23°C | 4.2 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 4 | |||
| -20°C | 4.2 | kJ/m² | ASTM D256 |
| -20°C | 5.0 | kJ/m² | ISO 179 |
| 23°C | 14 | kJ/m² | ISO 179 |
| 23°C | 13 | kJ/m² | ASTM D256 |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 1.26 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 1.47 | kJ/m² | ASTM D256 |
| Notched Izod Impact 5 | ISO 180 | ||
| -20°C | 1.2 | kJ/m² | ISO 180 |
| 23°C | 1.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 8.41 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 16.8 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -20°C | 9.0 | kJ/m² | ISO 180 |
| 23°C | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 109 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, not annealed | 62.8 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 63.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 154 | °C | ISO 306/A50, ASTM D1525 7 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+2 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 10 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 210 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 230 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | Flow |
| 2 . | Flow |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-306 (Comp) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| SABIC® HDPE F4520 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Akulon® K224-G6U | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Di-Pak™ R-4200 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Karina CRYSTAL PVC COMPOUND -E 802-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |