DOMAMID® A1-008-V30-H2-DB
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0DAKW_DOMAMID-A1-008-V30-H2-DB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity, 30% glass fiber reinforced, heat stabilised, deep black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 0.95 | % | |
| Flow : 23°C, 72 hr | 0.35 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 30 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 170 | MPa | |
| Break | 170 | MPa | |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/1A/20 |
| Flexural Modulus 2 | 7300 | MPa | ISO 178 |
| Flexural Stress 3 | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP7240 | Spartech Polycom | PP Copolymer | Spartech |
| Nycast CP | Cast Nylons Ltd. | Nylon 6 | Nycast |
| Jackdaw PLA HS10VN6587 | Jackdaw Polymers | PLA | Jackdaw PLA |
| Karina CRYSTAL COMP. PVC -E 68/208-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupox® SG3180S | LG Chem Ltd. | PBT+PET | Lupox® |