NOVAPOL® LF-Y819 Series
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | T0CzSt_NOVAPOL-LF-Y819-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LF-Y819-A (Base resin): Industrial packaging, shrink film, blends with LLDPE, small diameter pipe and tubing LF-Y819-C (Antiblock): Industrial packaging, liners, shrink film, blends with LLDPE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | > 25µm | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 180 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 225 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 13.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 29.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 21.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 170 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 490 | % | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, blown film | 180 | g | ASTM D1922 |
| TD : 38 µm, blown film | 130 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 30 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 19 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (38.0 µm) | 210 | J/cm | Internal method |
| Extrusion instructions |
|---|
| Optimum Blow-up Ratio: 2:1 to 3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veradel® A-304P | Solvay Specialty Polymers | PESU | Veradel® |
| VITAMIDE® BS10VN6607 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Adiprene® LFP 3940A | Chemtura | PUR-PC/PPDI | Adiprene® |
| LNP™ LUBRILOY™ R2000A compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Axiall PVC 8266 Natural 01 | Axiall Corporation | PVC, Rigid | Axiall PVC |