Jamplast JPHIPSE
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SzNBaP_Jamplast-JPHIPSE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPHIPSE is a high impact polystyrene with an excellent balance of flow, toughness, stiffness and heat resistance as compared to other HIPS resins. It is appropriate for extrusion applications where stiffness and toughness combined with trimmability are important. JPHIPSE is also commonly used for deep draw thermoforming and injection molding. A major use of this product is in appliances and housewares as well as food packaging and disposables applications such as cups, lids and serviceware. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| L-Scale | 60 | ||
| R-Scale | 95 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1650 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 19.3 | MPa | |
| Break | 24.1 | MPa | |
| Tensile Elongation 3(Break) | 52 | % | ASTM D638 |
| Flexural Modulus 4 | 1910 | MPa | ASTM D790 |
| Flexural Strength 5 | 42.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | ASTM D256 | ||
| -18°C, 3.18 mm | 64 | J/m | |
| 23°C, 3.18 mm | 110 | J/m | |
| Gardner Impact (23°C) | 18.1 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 87.2 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 73.9 | °C | |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 |
| CLTE - Flow (-40 to 82°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm, ALL) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 177 to 232 | °C | |
| Front Temperature | 191 to 260 | °C | |
| Mold Temperature | 21.1 to 65.6 | °C | |
| Injection Pressure | 34.5 to 276 | MPa | |
| Back Pressure | 0.0689 to 3.45 | MPa | |
| Clamp Tonnage | 2.8 to 5.5 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 1.3 mm/min |
| 5 . | Type I, 1.3 mm/min |
| 6 . | 0.25 mm Notch Depth |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1085 TFE 13 SI 2 | RTP Company | PBT | RTP |
| Tenac™ LT805 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| TEKNIFLEX® VA1260 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| Vi-Chem PVC V143-90E-8798 | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| Titacon® TR720 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |