Infino LP-3300
| Category: | PC , Polycarbonate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SzDgY6_InfinoLP3300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino LP-3300 is a polycarbonate (PC) product that contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical/electronic applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.10 - 0.30 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.10 - 0.30 | % | ISO 2577 |
| Traffic : 3.20mm | 0.10 - 0.30 | % | ISO 2577 |
| Ash Content | 34 | % | ASTM D5630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 115 | ASTM D785 | |
| R scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6300 | MPa | ASTM D638 |
| -- | 6200 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 91.0 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 91.0 | MPa | ASTM D638 |
| Fracture | 95.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 4 | 2.8 | % | ASTM D638 |
| Fracture | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 6200 | MPa | ASTM D790 |
| -- 6 | 6100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 120 | MPa | ASTM D790 |
| -- 8 | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 98 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 98 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 149 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 148 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 142 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 141 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity (25°C) | 3.50 | ASTM D150, IEC 60250 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultraform® N 2640 Z4 | BASF Corporation | Acetal (POM) Copolymer+PUR | Ultraform® |
| ACCUTECH™ HP0336C20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Bergamid™ A70 G33 TM-X BK079 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| BLUESTAR® PBT 403HF-G20 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Eastar™ DN011 | Eastman Chemical Company | Copolyester | Eastar™ |