POCAN® B 3215 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SySVz7_POCAN-B-3215-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 10 % glass fibers, injection molding |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.38 1.38 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.1 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.90 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 150 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4750 | MPa | ASTM D638 |
| 23°C | 4900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break, 23°C | 95.1 | MPa | ASTM D638 |
| Break, 23°C | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 23°C | 3990 | MPa | ASTM D790 |
| 23°C 5 | 4600 | MPa | ISO 178/A |
| Flexural Strength | |||
| 23°C | 138 | MPa | ASTM D790 |
| 3.5% Strain, 23°C | 135 | MPa | ISO 178/A |
| 23°C 6 | 145 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength (23°C) 7 | 5.1 | % | ISO 178/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halving Interval | IEC 60216 | ||
| Electric Strength | 11.4 | °C | |
| Tensile Impact Strength | 9.3 | °C | |
| Tensile Strength | 14.0 | °C | |
| Temperature Index | IEC 60216 | ||
| Electric Strength, 20000 hr | 160 | °C | |
| Tensile Impact Strength, 20000 hr | 140 | °C | |
| Tensile Strength, 20000 hr | 150 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Electrolytical Corrosion (23°C) | A 1 | IEC 60426 | |
| ISO Shortname | PBT, GHMR, 09-050, GF10 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | < 10 | kJ/m² | |
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30°C | 1.50 | J | |
| 23°C | 1.50 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B120 |
| Ball Pressure Test (212°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature 8 | 222 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | cm/cm/°C | |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 23°C, 100 Hz | 3.60 | ||
| 23°C, 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 23°C, 100 Hz | 1.5E-3 | ||
| 23°C, 1 MHz | 0.018 | ||
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207D TFE 15 | RTP Company | Nylon 612 | RTP |
| Sinpolene TPP1040 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Dugdale PVC Static Flexible PVC Nitrile Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Sylvin 8784-77 Grey 9453 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ KP002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |