TEKNIFLEX® VA1060 ALU
| Category: | Film, PVC/PCTFE , PVC/PCTFE Film |
| Manufacturer: | Tekni-Films, a div of Tekni-Plex |
| Trademark: | TEKNIFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SyNgVm_TEKNIFLEX-VA1060-ALU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tekniflex® VA series are designed for thermoforming blister packaging for Pharmaceutical products requiring high barrier to moisture. Thermoformable into small/medium cavities; FDA, EU, USP & EP compliant, Pharmaceutical-grade PCTFE film lamination. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | |
| Dimensional Stability 1(140°C) | -4.0 to 4.0 | % |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Film Thickness 2 | 269 | µm | |
| Yield | 2.45 to 3.00 | m²/kg |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Roll Width 3 | < 110.00 | cm | |
| Thermoforming Molding Temperature | 100 to 160 | °C |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 37.9 | MPa | |
| Oxygen Transmission Rate (23°C, 100% RH) | 19 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.39 | g/m²/24 hr |
| Note Message | |
|---|---|
| 1 . | 30 minutes |
| 2 . | Thickness tolerance: ±10% |
| 3 . | Roll width tolerance: ±1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bayfit® 49BM02(85 Index, 79 kg/m³) | Covestro - PUR | PUR, Unspecified | Bayfit® |
| Caltex PP HLG75 | GS Caltex | PP, Unspecified | Caltex PP |
| Daelim Po1y® PP-197 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Evoprene™ G 940 | AlphaGary | SEBS | Evoprene™ G |
| Karina WHITE PVC COMP E 880-10/136-A-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |