Grilon® TSGL-60/4 black 9833
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SwiID6_Grilon-TSGL-60-4-black-9833.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilon® TSGL-60/4 black 9833 is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 60% long glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Grilon® TSGL-60/4 black 9833: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.68 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.20 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 350 | 240 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 22500 | 17000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 275 | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 2.2 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 35 | 40 | kJ/m² | |
| 23°C | 35 | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | 90 | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 255 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 235 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 120 to 130 | -- | °C | |
| -- 2 | 220 | -- | °C | |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA66+PA6, MH, 14-220N, GF60 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 8520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Moplen RP2795 | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Xuchuan XCS-3991 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Daelim Po1y® XP9020 | DAELIM INDUSTRIAL CO., LTD. | mHDPE | Daelim Po1y® |
| SQUARE® LIM3919-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |