LG ABS HF380G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SvqSPC_LG-ABS-HF380G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS HF380G is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG ABS HF380G are:
Typical application of LG ABS HF380G: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 53 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2150 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 43.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 3.20 mm) | 70.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | |
| -30°C, 6.40 mm | 120 | J/m | |
| 23°C, 3.20 mm | 260 | J/m | |
| 23°C, 6.40 mm | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 88.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 85.0 | °C | |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 6 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 34 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 230 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide AW-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Bayflex® 180 RRIM (20% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| Etinox® EI-6310 | Ercros, S.A. | PVC, Flexible | Etinox® |
| KMI PP KM093-JM | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Sylvin 2990-76 Blue 8474 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |