Adiprene® L 167
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SvKgf2_Adiprene-L-167.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADIPRENE® L 167 urethane rubber is one of a series of liquid urethane polymers which can be cured to a strong, rubbery solid by reaction of the isocyanate groups with polyamine or polyol compounds. When cured with MBCA curing agent, ADIPRENE L 167 yields vulcanizates in the 95A durometer hardness range. Lower hardness values and special properties can be obtained with other curing systems. Cured ADIPRENE L 167 has high tensile strength and resilience and excellent properties at low temperatures. It is resistant to abrasion, compression set, oils, solvents, oxidation and ozone. ADIPRENE L 167 can be cast or sprayed to produce a variety of molded goods and protective and decorative coatings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 12.4 | MPa | |
| 300% Strain | 23.4 | MPa | |
| Tensile Strength | 34.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 87.6 | kN/m | ASTM D624 |
| Split | 26 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 40 | % | ASTM D395B |
| Bayshore Resilience | 40 | % | ASTM D2632 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -57°C | 552 | MPa | |
| -40°C | 114 | MPa | |
| -18°C | 49.3 | MPa | |
| 24°C | 16.5 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| CLTE - Flow | ASTM D696 | ||
| -36 to 0°C | 2.3E-4 | cm/cm/°C | |
| 0 to 24°C | 1.6E-4 | cm/cm/°C | |
| 24 to 100°C | 1.6E-4 | cm/cm/°C | |
| 100 to 150°C | 1.2E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.12 | W/m/K | ASTM C177 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 19 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life (85°C) | 6.0 | min | |
| Demold Time (100°C) | 15 | min | |
| Post Cure Time (70°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Abrasion Index - NBS | 300 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 1.0 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ratron® 250C6-WR | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| Shandong Aobang TPU-Polyester 75-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| TECHNAMID® A A-SV30-A-LOT | Poly Plastic | Nylon 66 | TECHNAMID® A |
| Wondel® C CTA | Nanjing Julong Engineering Plastics Co., LTD | PC+PBT | Wondel® C |
| Braskem PE SGF4960 | Braskem | HDPE | Braskem PE |