Torelina® A625H-L01
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SulqLE_Torelina-A625H-L01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torelina® A625H-L01 is a Polyphenylene Sulfide (PPS) product filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.84 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.85 | % | |
| Flow : 3.00 mm 2 | 0.25 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 13000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 36 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.4E-5 | cm/cm/°C | |
| Transverse | 3.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.360 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 3(320°C, 1.00 mm) | 130 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3703C | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 4007 MS | RTP Company | PPA | RTP |
| Axiall PVC 54915 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Comtrex Flexible PVC® 63XCF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| Sylvin 9812-75 Green 3193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |