LNP™ LUBRICOMP™ FX04491H compound
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SuOrcu_LNP-LUBRICOMP-FX04491H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* FX04491H is a compound based on Polyethylene resin containing Proprietary Fillers. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound PDX-F-04491 Product reorder name: FX04491H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.932 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.4 | % | |
| Across Flow : 24 hr | 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 7.4 | % | ASTM D638 |
| Flexural Modulus | 10700 | MPa | ASTM D790 |
| Flexural Strength | 23.4 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.13 | ||
| vs. Itself - Static | 0.11 | ||
| Wear Factor - Washer | 24.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 46 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 42.2 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 210 to 221 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 37.8 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 1528 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Vi-Chem PVC VNC101E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Geon™ Vinyl Flexible B5DW2 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ THERMOCOMP™ JF004Z compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |
| Sylvin 9604-90 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |