AKROMID® B3 GF 35 1 natural (2465)

Category: Nylon 6 , Polyamide 6
Manufacturer: AKRO-PLASTIC GmbH
Trademark: AKROMID®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: Su3Pw1_AKROMID-B3-GF-35-1-natural-2465-.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
AKROMID® B3 GF 35 1 natural (2465) is a 35% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength and light inherent color

Applications are mainly components in mechanical engineering and in the automotive industry
General Information
Filler / Reinforcement
  • Glass Fiber, 35% Filler by Weight
Features
  • High Rigidity
  • High Strength
Uses
  • Engineered Applications
Appearance
  • Natural Color
Resin ID (ISO 1043)
  • PA6 GF35
PhysicalDryConditionedUnitTest Method
Density (23°C)1.41--g/cm³ISO 1183
Spiral Flow 61.0--cmInternal Method
Molding Shrinkage ISO 294-4
     Across Flow 0.80--%
     Flow 0.10--%
Water Absorption (Saturation, 23°C)5.9 to 6.5--%ISO 62
Humidity Absorption - 62% RH (70°C)1.8 to 2.1--%ISO 1110
Additional InformationDryConditionedUnitTest Method
Reinforcement Content 35--%ISO 1172
HardnessDryConditionedUnitTest Method
Ball Indentation Hardness (H 961/30)240--MPaISO 2039-1
MechanicalDryConditionedUnitTest Method
Tensile Modulus 115007300MPaISO 527-2/1
Tensile Stress (Break)195120MPaISO 527-2/5
Tensile Strain (Break)3.05.0%ISO 527-2/5
Flexural Modulus 110000--MPaISO 178
Flexural Stress 2285--MPaISO 178
ImpactDryConditionedUnitTest Method
Charpy Notched Impact Strength ISO 179/1eA
     -30°C 13--kJ/m²
     23°C 1521kJ/m²
Charpy Unnotched Impact Strength ISO 179/1eU
     -30°C 90--kJ/m²
     23°C 100110kJ/m²
ThermalDryConditionedUnitTest Method
Heat Deflection Temperature
     0.45 MPa, Unannealed 220--°CISO 75-2/B
     1.8 MPa, Unannealed 215--°CISO 75-2/A
     8.0 MPa, Unannealed 165--°CISO 75-2/C
Melting Temperature 3220--°CDIN EN 11357-1
ElectricalDryConditionedUnitTest Method
Surface Resistivity 1.0E+121.0E+10ohmsIEC 60093
Volume Resistivity 1.0E+131.0E+10ohms·cmIEC 60093
Comparative Tracking Index (Solution A)600--VIEC 60112
FlammabilityDryConditionedUnitTest Method
Burning Rate 4(1.00 mm)< 100--mm/minFMVSS 302
Flame Rating (0.800 mm)HB--UL 94
Glow Wire Flammability Index (1.60 mm)650--°CIEC 60695-2-12
Note Message
1 .2.0 mm/min
2 .2.0 mm/min
3 .10 K/min, DSC
4 .>1 mm
Resin Grade Manufacturer Category Trademark
Marlex® 9514H Chevron Phillips Chemical Company LLC HDPE, HMW Marlex®
TIPPLEN® R 780 MOL Petrochemicals Co. Ltd. PP Random Copolymer TIPPLEN®
BESTDUR TPXG6/02 Triesa Plastics PBT+PET BESTDUR
Braskem PE SLL118/21 Braskem LLDPE Braskem PE
ELASTOSIL® LR 3040/60 A/B Wacker Chemie AG Silicone ELASTOSIL® LR